Stabilized polyacrylonitrile compositions with sulfur-phosphorus containing material

ABSTRACT

A method of forming stabilized polyacrylonitrile compositions which are particularly suited for the spinning of polyacrylonitrile fibers and films and the compositions produced thereby wherein acrylonitrile polymers containing at least 85 percent acrylonitrile are dissolved in a solvent which is acetonitrile or an acetonitrile - water mixture and which contains as a color stabilizer a compound having the following general formula:   WHEREIN R1, R2, and R3 are monovalent organic radicals which may be substituted or unsubstituted independently selected from the group consisting of alkyl, cycloalkyl, aryl, and combinations thereof. Preferably, the solvent and polymer are purged with nitrogen and the pH of the solvent is adjusted to about 6.0 7.0.

United States Patent Thompson Aug. 28, 1973 STABILIZED POLYACRYLONITRILE COMPOSITIONS WITH SULFUR-PHOSPHORUS CONTAINING MATERIAL Inventor: Darrell R. Thompson, Somerville,

Celanese Corporation, New York, N.Y.

Filed: Apr. 22, 1971 Appl. No.: 136,621

Assignee:

US. Cl. 260/29.6 AN, 260/29.6 MQ, 260/29.6 MP,

Int. Cl. C08f 45/24 Field of Search 260/29.6 R, 29.6 AN, 260/29.6 MQ. 29.6 MP, 32.4, 45.7 PS

References Cited UNITED STATES PATENTS 9/1969 Nakanome et a1 260/29.6 AN 10/1950 Caldwell 260/29.6 AN 7/1965 Coover et a1. 260/29.6 AN 1/1972 Nakanome et a1 260/29.6 AN

Primary Examiner-Harold D. Anderson Att0rney-Thomas .1. Morgan, Herbert M. Adrian, Jr. and Andrew F. Sayko, Jr.

[57] ABSTRACT wherein R,, R and R are monovalent organic radicals which may be substituted or unsubstituted independently selected from the group consisting of alkyl, cycloalkyl, aryl, and combinations thereof. Preferably, the solvent and polymer are purged with nitrogen and the pH of the solvent is adjusted to about 6.0 7.0.

23 Claims, No Drawings STABILIZED POLYACRYLONITRILE COMPOSITIONS WITI-I SULFUR-PHOSPIIORUS CONTAINING MATERIAL BACKGROUND OF THE INVENTION This invention relates to the stabilization of polyacrylonitrile compositions. More particularly, the invention relates to the stabilization of polyacrylonitrile compositions containing a low-boiling solvent, which compositions are particularly useful for the formation of shaped articles such as fibers and films and which have a tendency to develop color either upon standing or upon the application of heat.

The terms polyacrylonitrile" and acrylonitrile polymers as used herein refer to homopolymers as well as copolymers of acrylonitrile containing at least about 85 percent by weight acrylonitrile and up to about percent by weight of at least one other ethylenically unsaturated compound copolymerizable with acrylonitrile.

The utility of acrylonitrile polymers is wellestablished, particularly for the preparation of such shaped articles as fibers and films. However, preparative techniques generally are restricted to dry spinning and wet spinning from solutions having a polymer concentration up to about to percent by weight. Conventional spinning technology, dry spinning in particular, has utilized relatively high boiling solvents, e.g., boiling above about 100 C., for forming spinnable dopes of acrylonitrile polymers. The formation of shaped articles by a melt extrusion process, that is, a process in which the polymer is melted and the molten polymer extruded through a die or spinnerette into an inert medium in contradistinction to dry and wet spinning methods in which a solution of the polymer is extruded through a die or spinnerette, is not practical be- I cause of the relatively high melting temperatures of acrylonitrile polymers containing at least 85 percent by weight acrylonitrile and because of the tendency of such polymers to decompose before or during melting.

Acrylonitrile polymers having an acrylonitrile content of at least 85 percent generally are insoluble in the more common solvents. Whenever suitable solvents have been found, however, the application of heat usually is necessary in order to effect solution. The application of heat to effect solution usually results in the development of a pale yellow color in the resultant solution, which color generally darkens and becomes brown with time. Even without the application of heat or upon removal of heat after a solution has been obtained, color develops in solutions upon standing for prolonged periods of time. Color development is more pronounced at elevated temperatures and in the presence of bases or other strong nucleophiles. Color development is most severe in N,N-dimethylfonnamide solutions such as those employed in dry spinning. Obviously, any color developed in polymer solutions or spinning dopes will be carried over into the products formed therefrom.

The mechanism responsible for color formation and the nature of the chromophores involved still are uncertain. The color may be caused by the presence of metal ions such as iron, copper, and manganese in the polymer solutions. Impurities other than metal ions present in the solvents also have been cited as a cause. The employment of amides, such as N,N-dimethylformamide, as solvents may result in the thermal decomposition of the solvent to give amines which in turn may cause color formation. Or, color formation may be caused by conjugation of carbon-nitrogen double bonds derived from the cyanide groups in the polyacrylonitrile. Such conjugated double bonds conceivably may result from a cyclization reaction initiated perhaps by oxidation products, such as hydroperoxides, in the polymer. The resultant conjugated structures would be colored because of the low energy electronic transitions possible in the resonating double bond system. Regardless of the mechanism which gives rise to color in solutions of acrylonitrile polymers, e.g., spinning dopes, the presence of color in polymer solutions results in shaped articles which are colored. Such coloration is undesirable for aesthetic reasons and contributes to product non-uniformity.

SUMMARY OF THE INVENTION It is therefore an object of the present invention to provide stabilized polyacrylonitrile compositions containing a low-boiling solvent.

It is another object to prevent undesirable color formation in polyacrylonitrile compositions containing a low-boiling solvent.

Still another object of the present invention is to minimize color formation in polyacrylonitrile compositons containing a low-boiling solvent when such compositons either are permitted to stand for prolonged periods of time or are heated, either to effect solution of the polyacrylonitrile in the solvent or during spinning of said composition to provide shaped articles.

Yet another object is to provide stabilized polyacrylonitrile compositions containing a low'boiling solvent from which crystal-clear shaped articles may be prepared wherein clarity and freedom from color are independent of thickness, fiber denier, or the like.

It is also an object of the present invention to provide a method for preparing stabilized polyacrylonitrile compositons containing a low-boiling solvent, which compositions are particularly suited for the formation of shaped articles of polyacrylonitrile.

Yet another object is to provide a method for preparing stabilized polyacrylonitrile compositions containing a low boiling solvent, which solvent is acetonitrile or an acetonitrile water mixture and which compositions can, if desired, be stored or shipped as a solid or gelled material and subsequently formed into a spinning solution or dope for the preparation of polyacrylonitrile fibers and films.

These and other objects will be apparent to those skilled in the art from a consideration of the description and claimsof the invention which follow.

In accordance with the present invention, stabilized polyacrylonitrile compositions containing a low-boiling solvent are obtained by the process which comprises the steps of adding a minor amount of a stabilizing compound to a solvent which is acetonitrile or an acetonitrile water mixture containing up to about 40 weight percent water, adding acrylonitrile polymer to the solvent stabilizer mixture, and heating and mixing the polyacrylonitrile solvent stabilizer mixture under superatmospheric pressure to a temperature above about the boiling point at atmospheric pressure of said solvent and below the degradation temperature of the polyacrylonitrile, i.e., within the range from about to C., to produce a solution. The resultant solution then can be cooled to a temperature below its original solubilizing temperature and above about the boiling point at atmospheric pressure of said solvent without gelation occurring. Cooling the resul-. tant solution to a temperature below about the boiling point at atmospheric pressure of said solvent, e.g., to ambient temperature, results in the gelation of said solution. Preferably, the stabilizing compound is added to said solvent prior to the addition of the polyacrylonitrile to said solvent. Also, the solvent and polyacrylonitrile preferably are purged separately with nitrogen and the pH of the solvent is adjusted to about 6.0 7.0.

While the present invention contemplates the use of acetonitrile alone as solvent, it is preferred that an acetonitrile water mixture be employed as solvent wherein said solvent contains up to about 50 percent water, based on the weight of acetonitrile. Spinning solutions of a stabilized polyacrylonitrile composition of the present invention are obtained by maintaining said composition under sufficient superatrnospheric pressure to permit the maintenance of said composition at a temperature above the gel temperature of said composition without distillation of said solvent, said gel temperature being near to but below the boiling poin at atmospheric pressure of said solvent.

The aforementioned stabilizing compound is a compound having the following general formula:

i P-S 1 wherein R R and R are monovalent organic radicals which may be substituted or unsubstituted independently selected from the group consisting of alkyl, cycloalkyl, aryl, and combinations thereof. The number of carbon atoms contained in any given radical is in the range of from about six to about 20.

DETAILED DESCRIPTION OF THE INVENTION As indicated hereinbefore, stabilized polyacrylonitrile compositions containing a low-boiling solvent are obtained by the inclusion in said compositions of a minor amount of a sulfur-and phosphorous containing material. By a minor amount is meant less than about percent, based on the weight of polyacrylonitrile, preferably less than about 5 percent, and most preferably in the range of from about 0.01 percent to about 3.0 percent. The monovalent organic radicals R R and R of said sulfurand phosphorous containing material usually will be the same and preferably will be an alkyl or alkaryl radical. Examples of suitable materials include, among others, trihexyl trithiophosphite, trioctyl trithiophosphite, tridecyl trithiophosphite, trilauryl trithiophosphite, tricetyl trithiophosphite, tristearyl trithiophosphite, tri(2-ethylhexyl) trithiophosphite, trichlorolauryl trithiophosphite, tricyclohexyl trithiophosphite, triphenyl trithiophosphite, trinaphthyl trithiophosphite, tri( hydroxyphenyly trithiophosphite, tri( methoxyphenyl) trithiophosphite, tri(dihydroxyphenyl) trithiophosphite, tri(diethoxyphenyl) trithiophosphite, tri(carboxyphenyl) trithiophosphite, tribenzyl trithiophosphite, tri(hexylphenyl) trithiophosphite, tri(decylphenyl) trithiophosphite, tri(benzoylphenyl) trithiophosphite, phenyl didecyl trithiophosphite, diphenyl lauryl trithiophosphite, and the like. Examples of preferred compounds include trioctyl trithiophosph- 4 ite, tridecyl trithiophosphite, trilauryl trithiophosphite, tricety] trithiophosphite, tristearyl trithiophosphite, tri(hexylphenyl) trithiophosphite, and tri(decylphenyl) trithiophosphite, with trilauryl trithiophosphite being most preferred.

The sulfurand phosphorous containing stabilizers of the present invention have in the past found utility as stabilizers for polyethylene and polypropylene, albeit usually in the presence of one or more required or preferred compounds (U.S. Pat. Nos. 3,179,621 and 3,256,237). In view of the entirely different nature of polyethylene and polypropylene as compared with the polyacrylonitrile compositions of the present invention, the stabilizing effect of said stabilizers is indeed surprising and a theoretical basis for same is not apparent. Also surprising is the fact that said stabilizers effectively stabilize the polyacrylonitrile compositions of the present invention in the absence of any other compound or compounds.

The presence of the sulfurand phosphorous containing stabilizers of the present invention in polyacrylonitrile compositions containing a low-boiling solvent effectively minimizes color formation in said compositions, even when said compositions are exposed to heat. The effectiveness of said stabilizers, however, usually may be improved by excluding oxygen from said compositions and by adjusting the pH of the solvent to about 6.0 7.0. Although various means for excluding oxygen from said compositions and for adjusting the pH of the solvent will be obvious to those skilled in the art, the following procedure is both satisfactory and preferred. The sulfur containing stabilizer is dissolved in the solvent at ambient temperature. The pH of the resulting solution then is adjusted to 6.0 7.0 by adding concentrated sulfuric acid. Both dissolved and atmospheric oxygen are displaced by bubbling nitrogen through the pH adjusted solution.

Separately, polyacrylonitrile powder is placed in a vacuum chamber and the chamber evacuated. Nitrogen then is introduced into the chamber. This procedure of evacuation and nitrogen purging is repeated several times as necessary. The polymer and pH adjusted solution then are brought together and heated under a nitrogen atmosphere to effect solution. The resultant stabilized polyacrylonitrile composition then is either stored or used directly to prepare shaped articles.

As stated hereinbefore, the present invention is directed to the formation of stabilized polyacrylonitrile compositions wherein the polyacrylonitrile contains at least percent acrylonitrile. These acrylonitrile polymers can be acrylonitrile homopolymers as well as copolymers of two or more monomers wherein up to about 15 percent of the polymer can be another ethylenically unsaturated compound which is copolymerizable with acrylonitrile. Such materials, which can be monomers or polymers which are copolymerizable with the acrylonitrile, usually are added to modify and/or enhance certain characteristics of the polyacrylonitrile or shaped articles made therefrom. Often the material copolymerized withthe acrylonitrile contains a chemical group which increases the basic dyeability of the resulting polymer. Such dyeability enhancing compounds nonnally contain sulfur or phosphorous in the ethylenically unsaturated material copolymerizable with the acrylonitrile. Typically, such sulfur-or phosphorous containing compounds are added in an amount of from about 0.1 to about 5 percent by weight based on the weight of the total polymer composition. Other modifying substances usually are used in amounts up to about percent. Typical ethylenically unsaturated monomers copolymerizable with acrylonitrile include, among others, methyl acrylate, vinyl acetate, vinylidene chloride, methyl methacrylate, methallyl alcohol, vinylidene cyanide, styrene sulfonic acids, sodium methallylsulfonate, mixtures and partial polymers thereof, and the like, all of which are well known to those skilled in the art. Similarly, acid dyeability may be imparted to the polyacrylonitrile by the use of aminecontaining comonomers such as allylamine. The polymers are obtained by conventional methods which are well known in the art.

The degree to which the polymer is polymerized is dependent upon the end use for which the polymer is intended. Thus, for the spinning of polyacrylonitrile fibers, the polymer preferably is polymerized to an inherent viscosity (measured at C. in dimethyl formamide) of from about 0.5 to about 2.5 and more preferably from about 1.2 to about 1.8. Of course, polymers having higher inherent viscosities can be used, resulting in higher solution viscosities for a given solvent concentration; higher inherent viscosities also may result in a loss or reduction of certain desirable properties, auch as abrasion resistance, fibrillation, and the like.

In most instances wherein the present compositions are most desirably used, solutions having a high concentration of solids are preferred. With the present solvent system and process, solutions having a high concentration of solids are readily obtained with acrylonitrile polymers having inherent viscosities in the range normally used for commercial fiber spinning, i.e., from about 1.2 to about 1.8. In particular, solutions having a solids content of from about to about 70 percent by weight are readily obtained. The more preferred spinning solutions have a solids content in the range of from about to about 55 percent with polymers having inherent viscosities of from about 1.2 to about 1.8 or higher. With polymers having lower inherent viscosities, e.g., from about 0.5 to about 1.2, solutions having a solids content of up to about 70 percent or higher can be obtained.

The solvent may be acetonitrile alone or more preferably an acetonitrile water mixture. The addition of water to acetonitrile lowers both the gel temperature of the polymer solution and the initial solution temperature of the polymer. Therefore, in the solvent portion, it is preferable to use up to about 50 weight percent of water based on the weight of acetonitrile, more preferably from about 2 to about 40 weight percent water, and most preferably from about "18 to about 35 weight percent water. In the most preferred range of water content, the lowest solution viscosities for a given polymer are obtained.

At atmospheric pressure, the boiling point of acetonitrile is about 82 C. and that of the azeotrope of 15 percent water is about 76 C. To form the initial solution, temperatures in excess of the boiling temperature of acetonitrile are used, particularly for the more difficultly soluble acrylonitrile polymers. Consequently, the process is operated under superatmospheric pressure which can be either an applied pressure or the solvent vapor pressure which is developed autogenously at the elevated temperatures. The pressure employed preferably is that required to maintain the solvent primarily in the liquid phase at the solvating. temperature. This required pressure increases with increasing temperatures and is in the range of from about 30 to about 40 pounds per square inch gauge at about 100 C. Thus, solvation preferably is conducted in a pressure unit or sealed system to prevent the escape of solvent vapor and to maintain the solvent in the liquid phase.

The solvation temperature required to obtain the compositions of the present invention will vary with the proportions of acetonitrile and water and with the proportion and kind of polyacrylonitrile, within the range of from about to about 160 C. Once solvation is attained, however, the temperature of the composition can be reduced to the desired holding or spinning temperature. Reducing the temperature of the composition below about 80 C., again depending upon the nature of the composition, results in the gelling of the composition. Accordingly, the composition can be either cooled and retained in a gelled state for storage or shipment or maintained in the temperature range of from about 80 C. to the degradation temperature of the polymer. If the composition is stored as a gel, it is preferred to retain the composition in a sealed container to reduce or eliminate the gradual loss of solvent therefrom over a period of time.

It may be pointed out that the compositions of the present invention are remarkably stable to prolonged heating. By way of illustration, a-composition consisting of 40 weight percent of a polyacrylonitrile comprised of percent by weight of acrylonitrile and 60 weight percent of an acetonitrile water mixture containing 22 percent water shows practically no change in viscosity after three days at C.

The following examples will serve to illustrate the invention without intending to limit it in any manner.

EXAMPLE I To an autoclave having a stirring means and a heating means and fitted with a condenser and a nitrogen inlet tube extending to the bottom of the vessel are added 60 parts of a solvent consisting of 80 percent by weight acetonitrile and 20 percent by weight water and 0.2 parts (0.5 weight percent, based on the weight of polyacrylo nitrile) of trilauryl trithiophosphite. The mixture is stirred at ambient temperature until a solution is obtained. The autoclave then is charged with 40 parts of polyacrylonitrile powder characterized as follows:

95 percent polyacrylonitrile 4.8 percent methyl acrylate 0.2 percent sodium methyl allyl sulfonate The polymer-solvent mixture is heated at 85 C. and under a pressure of 2,500 mm mercury for 0.5 hours. The resultant solution, which is slightly turbid and comprised of 40 percent solids, has a color rating of 7 after 24 hours at 1 10 C.

Color rating is determined by comparing the polymer solution with a series of color tubes containing increasing concentrations of a yellow-brown dye, lrgacet Yellow 2RL, in N,Ndimethylfonna.mide. Tube number 1 contains only solvent. Tube number 2 contains 1.0 X 10 percent by weight of the dye. The concentration of dye in each succeeding tube increases by 1.0 X 10 weight percent, so that the dye concentration in any given tube is given by (tube number l) X 10 weight percent.

For control purposes, the procedure of Example 1 is repeated, except that the addition of benzenethiol is omitted. After 24 hours at 110 C., the polymer solution has a color rating of 4].

EXAMPLE 2 The procedure of Example 1 is repeated, except that the trilauryl trithiophosphite is replaced with an equal amount of tricetyl trithiophosphite. The polymer solution is slightly turbid and has a color rating of 16 after 24 hours at 110 C.

EXAMPLE 3 The procedure of Example 1 is repeated, except that the trilauryl trithiophosphite is replaced with an equal amount of trioctyl trithiophosp'hitefi-After 24 hours at 1 10 C., the polymer solution has a color rating of 16.

EXAMPLE 4 The procedure of Example 3 is repeated with similar results, except that the trioctyl trithiophosphite is replaced with an equal amount of triphenyl trithiophosphite.

EXAMPLE 5 The procedure of Example 3 is repeated with similar results, except that the trioctyl trithiophosphite is replaced with an equal amount of tricyclohexyl trithiophosphite.

EXAMPLE 6 The procedure of Example 3 is repeated with similar results, except that the trioctyl trithiophosphite is replaced with an equal amount of tri(decylphenyl) trithiophosphite.

EXAMPLE 7 The procedure of Example 3 is repeated, modified as follows: The amount of dioctyl trithiophosphite is reduced to 0.05 weight percent. The pH of the solvent stabilizer solution is adjusted to about 6.0 7.0 by the drop-wise addition of concentrated sulfuric acid. Nitrogen then is bubbled slowly through the solution to displace dissolved and atmospheric oxygen. During this time, a vacuum chamber is charged with the polyacrylonitrile powder, evacuated, and nitrogen introduced until atmospheric pressure is attained. The evacuation nitrogen introduction cycle is repeated two more times. The polyacrylonitrile powder then ischarged to the autoclave under a nitrogen purge; during preparation of the polymer solution, a nitrogen atmosphere is maintained in the autoclave. The color rating of the resultant polymer solution after 24 hours at 1 C. is approximately equivalent to that of the polymer solution of Example 3.

From a reading of the present disclosure, various changes and modifications in the disclosed process will be obvious to those skilled in the art. For example, the pH adjustment of the solvent may be accomplished by the addition of mineral acids other than sulfuric acid or by the addition of anhydrides of mineral acids. The pH adjustment of the solvent also may be accomplished by the use of organic acids, such as carboxylic acids and sulfonic acids. Alternatively, solvent pH control may be accomplished by the use of bases such as sodium hydroxide or by buffers of various types. Furthermore, exclusion of oxygen from the solvent may employ reduced pressures in conjunction with nitrogen purging. These and other changes and modifications by those skilled in the art are considered to be within the spirit and scope of the present invention.

Throughout the foregoing disclosure and the claims which follow, the compositions of the present invention are referred to as solutions of a polymer in a solvent. However, the exact nature of said compositions is not known. It does appear, though, that the acetonitrile portion of the solvent is absorbed by the polymer to fluidize it, rather than the polymer being dissolved in the solvent. Thus, at least in some instances, said compositions may deviate from typical solutions. In view of the uncertainties involved, the terminology employed is considered satisfactory since such terminology enables any person skilled in the art to make and use said compositions.

Having thus disclosed the invention, what is claimed 1. A stabilized film or fiber forming polyacrylonitrile composition consisting essentially of polyacrylonitrile containing at least 85 percent acrylonitrile and up to about 15 weight percent of at least one other ethylenically unsaturated material copolymerized therewith; acetonitrile-water mixtures, and from about 0.01 to about 3 weight percent, based on the weight of said polyacrylonitrile, of a sulfurand phosphorouscontaining stabilizer having the following general formula:

wherein R R and R are monovalent organic radicals independently selected from the group consisting of alkyl, cycloalkyl, aryl, and combinations thereof, with a number of carbon atoms contained in any given radical being in the range of from about 6 to about 20.

2. The stabilized film or fiber forming polyacrylonitrile composition of claim 1 wherein said polyacrylonitrile consists essentially of from about 30 to about percent of said composition.

3. The stabilized film or fiber forming polyacrylonitrile composition of claim 1 wherein said solvent contains up to about 50 percent water.

4. The stabilizedfilm or fiber forming polyacrylonitrile composition of claim 1 wherein R R and R of said stabilizer are the same monovalent organic radical selected from the group consisting of alkyl and alkaryl.

5. The stabilized film or fiber forming polyacrylonitrile composition of claim 1 wherein said stabilizer is trilauryl trithiophosphite.

6. The stabilized film or fiber forming polyacrylonitrile composition of claim 1 wherein said solvent contains from about 2 to about 35 percent water and R R and R of said stabilizer are the same monovalent organic radical selected from the group consisting of alkyl and alkaryl.

7. The stabilized film or fiber forming polyacrylonitrile composition of claim 6 wherein said polyacrylonitrile is a homopolymer.

8. The stabilized film or fiber forming polyacrylonitrile composition of claim 6 wherein at least one of the ethylenically unsaturated materials copolymerized with acrylonitrile is a sulfur-containing material.

9. The stabilized film or fiber forming polyacrylonitrile composition of claim 6 wherein at least one of the ethylenically unsaturated materials copolymerized with acrylonitrile is methyl acrylate.

10. A stabilized film or fiber forming polyacrylonitrile composition useful as a spinning solution for the production of polyacrylonitrile fibers wherein said composition consists essentially of polyacrylonitrile containing at least 85 percent acrylonitrile and up to about 15 weight percent of at least one other ethylenically unsaturated material copolymerized therewith, a solvent consisting essentially of acetonitrile and from about 2 to about 40 percent water, and from about 0.01 to about 3 weight percent, based on the weight of said polyacrylonitrile, of a sulfurand phosphorouscontaining stabilizer having the following general formula:

F IT-SR: SR3

wherein R,, R and R are the same monovalent organic radicals selected from the group consisting of alkyl and alkaryl, with the number of carbon atoms contained in any given radical being in the range of from six to about 20, and said composition is maintained under superatmospheric pressure at a temperature above about 80 C.

11. The stabilized film or fiber forming polyacrylonitrile composition of claim wherein said stabilizer is trilauryl trithiophosphite.

12. The stabilized film or fiber forming polyacrylonitrile composition of claim 10 wherein said superatmospheric pressure is greater than about the vapor pressure of said solvent at a temperature of from about 80 to about 160 C.

13. A stabilized film or fiber forming polyacrylonitrile composition consisting essentially of from about 30 to about 70 percent of polyacrylonitrile containing from 85 to about 99 percent acrylonitrile, from about 0 to about percent of an ethylenically unsaturated material copolymerized therewith, and from about 0.1 to about 2 percent of a sulfur-containing ethylenically unsaturated material also copolymerized therewith; from about 29 to about 69 percent of a solvent consisting of acetonitrile and from about 2 to about 40 percent water; and from about 0.01 to about 3 weight percent, based on the weight of said polyacrylonitrile, of a sulfurand phosphorous-containing stabilizer having the following general formula;

wherein R R and R are the same monovalent organic radical selected from the group consisting of alkyl and alkaryl, with the number of carbon atoms contained in any given radical being in the range of from about six to about 20, said composition being maintained under superatmospheric pressure greater than the vapor pressure of said solvent and at a temperature of from about 80 to about 160 C.

14. The stabilized film or fiber forming polyacrylonitrile composition of claim 13 wherein said stabilizer is trilauryl trithiophosphite.

15. A method of forming stabilized film or fiber forming polyacrylonitrile compositions which comprises the steps of adding to a solvent selected from acetonitrilewater mixtures a minor amount of sulfurand phosphorous-containing stabilizer having the following general formula:

wherein R,, R and R are monovalent organic radicals independently selected from the group consisting of alkyl, cycloalkyl, aryl, and combinations thereof, with the number of carbon atoms contained in any given radical being in the range of from about six to about 20; adding polyacrylonitrile which contains at least 85 percent acrylonitrile and up to about 15 weight percent of at least one other ethylenically unsaturated material copolymerized therewith; and heating and mixing the resultant mixture under superatmospheric pressure to a temperature above about C. and below the degradation temperature of said polyacrylonitrile to produce a solution.

16. The method of claim 15 wherein said solvent contains up to about 50 percent water.

17. The method of claim 15 wherein R,, R and R of said stabilizer are the same monovalent organic radicals selected from the group consisting of alkyl and al karyl in an amount ranging from about 0.01 to about 3 weight percent, based on the weight of said polyacrylonitrile.

18. The method of claim 15 wherein said stabilizer is trilauryl trithiophosphite.

19. The method of claim 15 wherein said superatmospheric pressure is greater than the vapor pressure of said solvent.

20. The method of claim 15 wherein oxygen is excluded and the pH of the solvent is adjusted to about 6.0 7.0.

21. The method of claim 15 wherein said polyacrylonitrile consists essentially of from about 30 to about 70 percent of said compositions.

22. A method of forming stabilized film or fiber forming polyacrylonitrile compositions which comprises the steps of adding from about 0.01 to about 3 weight percent, based on the weight of polyacrylonitrile, of a sulfurand phosphorous-containing stabilizer having the following general formula:

wherein R R and R are the same monovalent organic radicals selected from the group consisting of alkyl and alkaryl, with the number of carbon atoms contained in any given radical being in the range of from about six to about 20 to a solvent which consists of acetonitrile and from about 2 to about 40 percent water; adjusting the pH of the resulting solution to about 6.0 7.0; purging the resulting solution with nitrogen to exclude dissolved and atmospheric oxygen; adding polyacrylonitrile containing at least percent acrylonitrile and up to about 15 weight percent of at least one other ethylenically unsaturated material coabove about 80 C. and below the degradation temperpolymerized therewith, wherein said polyacrylonitrile mute f Said polyacrylonitrile has been purged and 23. The method of claim 22 wherein said stabilizer is the resultant mixture in nitrogen atmosphere under superatmospheric pressure which is greater than the 5 "ilauryl trithiophosPhite vapor pressure of said solvent and at a temperature 

2. The stabilized film or fiber forming polyacrylonitrile composition of claim 1 wherein said polyacrylonitrile consists essentially of from about 30 to about 70 percent of said composition.
 3. The stabilized film or fiber forming polyacrylonitrile composition of claim 1 wherein said solvent contains up to about 50 percent water.
 4. The stabilized film or fiber forming polyacrylonitrile composition of claim 1 wherein R1, R2, and R3 of said stabilizer are the same monovalent organic radical selected from the group consisting of alkyl and alkaryl.
 5. The stabilized film or fiber forming polyacrylonitrile composition of claim 1 wherein said stabilizer is trilauryl trithiophosphite.
 6. The stabilized film or fiber forming polyacrylonitrIle composition of claim 1 wherein said solvent contains from about 2 to about 35 percent water and R1, R2, and R3 of said stabilizer are the same monovalent organic radical selected from the group consisting of alkyl and alkaryl.
 7. The stabilized film or fiber forming polyacrylonitrile composition of claim 6 wherein said polyacrylonitrile is a homopolymer.
 8. The stabilized film or fiber forming polyacrylonitrile composition of claim 6 wherein at least one of the ethylenically unsaturated materials copolymerized with acrylonitrile is a sulfur-containing material.
 9. The stabilized film or fiber forming polyacrylonitrile composition of claim 6 wherein at least one of the ethylenically unsaturated materials copolymerized with acrylonitrile is methyl acrylate.
 10. A stabilized film or fiber forming polyacrylonitrile composition useful as a spinning solution for the production of polyacrylonitrile fibers wherein said composition consists essentially of polyacrylonitrile containing at least 85 percent acrylonitrile and up to about 15 weight percent of at least one other ethylenically unsaturated material copolymerized therewith, a solvent consisting essentially of acetonitrile and from about 2 to about 40 percent water, and from about 0.01 to about 3 weight percent, based on the weight of said polyacrylonitrile, of a sulfur- and phosphorous-containing stabilizer having the following general formula:
 11. The stabilized film or fiber forming polyacrylonitrile composition of claim 10 wherein said stabilizer is trilauryl trithiophosphite.
 12. The stabilized film or fiber forming polyacrylonitrile composition of claim 10 wherein said superatmospheric pressure is greater than about the vapor pressure of said solvent at a temperature of from about 80* to about 160* C.
 13. A stabilized film or fiber forming polyacrylonitrile composition consisting essentially of from about 30 to about 70 percent of polyacrylonitrile containing from 85 to about 99 percent acrylonitrile, from about 0 to about 15 percent of an ethylenically unsaturated material copolymerized therewith, and from about 0.1 to about 2 percent of a sulfur-containing ethylenically unsaturated material also copolymerized therewith; from about 29 to about 69 percent of a solvent consisting of acetonitrile and from about 2 to about 40 percent water; and from about 0.01 to about 3 weight percent, based on the weight of said polyacrylonitrile, of a sulfur- and phosphorous-containing stabilizer having the following general formula:
 14. The stabilized film or fiber forming polyacrylonitrile composition of claim 13 wherein said stabilizer is trilauryl trithiophosphite.
 15. A method of forming stabilized film or fiber forming polyacrylonitrile compositions which comprises the steps of adding to a solvent selected from acetonitrile-water mixtures a minor amount of sulfur- and phosphorous-containing stabilizer having the following general formula:
 16. The method of claim 15 wherein said solvent contains up to about 50 percent water.
 17. The method of claim 15 wherein R1, R2, and R3 of said stabilizer are the same monovalent organic radicals selected from the group consisting of alkyl and alkaryl in an amount ranging from about 0.01 to about 3 weight percent, based on the weight of said polyacrylonitrile.
 18. The method of claim 15 wherein said stabilizer is trilauryl trithiophosphite.
 19. The method of claim 15 wherein said superatmospheric pressure is greater than the vapor pressure of said solvent.
 20. The method of claim 15 wherein oxygen is excluded and the pH of the solvent is adjusted to about 6.0 - 7.0.
 21. The method of claim 15 wherein said polyacrylonitrile consists essentially of from about 30 to about 70 percent of said compositions.
 22. A method of forming stabilized film or fiber forming polyacrylonitrile compositions which comprises the steps of adding from about 0.01 to about 3 weight percent, based on the weight of polyacrylonitrile, of a sulfur- and phosphorous-containing stabilizer having the following general formula:
 23. The method of claim 22 wherein said stabilizer is trilauryl trithiophosphite. 